Cobalt-Chrome Sheet (CoCr Sheet)
Cobalt-Chrome Sheet: Versatile Flat Panels for Customizable Medical Implants
Cobalt-Chrome Sheet Description:
Flat cobalt-chrome panels, hot-rolled or forged, with thicknesses from 0,2 mm to 5 mm and dimensions up to 400 × 400 mm. L605 provides toughness, while MP35N enhances corrosion resistance for custom implants.
Cobalt-Chrome Sheet Key Features:
- High hardness (350–500 HV for L605, 400–550 HV for MP35N).
- Corrosion resistance in physiological environments.
- Machinable into complex shapes with tight tolerances.
Cobalt-Chrome Sheet Certification and Standards:
- ASTM F90 (L605): For CoCrWNi alloys.
- ASTM F562 (MP35N): For CoCrNiMo alloys.
- ASTM F1537: General wrought CoCrMo standard.
- ISO 5840, ISO 13485, and ISO 10993: For cardiovascular, quality, and biocompatibility.
Neden Kobalt-Krom?
Kobalt-krom'un gücü, aşınma direnci ve biyouyumluluğu—L605 ve MP35N gibi sınıflarla geliştirilmiş ve titiz standartlarla desteklenmiştir—onu tıbbi yenilikler için en iyi tercih haline getirir. Belirli uygulamalar veya özel çözümlerle mi ilgileniyorsunuz? Daha fazla bilgi için bize ulaşın!
Kobalt-krom (CoCr), genellikle molibden ile zenginleştirilmiş bir kobalt ve krom alaşımı olup, olağanüstü dayanıklılığı, korozyon direnci ve biyouyumluluğu nedeniyle değerlidir. 800–1500 MPa aralığında çekme dayanımı ve 300–550 HV sertliği ile CoCr, tıbbi teknolojide bir temel taşıdır. L605 (Co-Cr-W-Ni) ve MP35N (Co-Cr-Ni-Mo) gibi popüler sınıflar performansını yükseltir.
- Bone Plates: L605 sheets (1–3 mm thick, 50–200 mm long) stabilize fractures under 600 N.
- Dental Frameworks: MP35N sheets (0,5–1 mm) form bridges and crowns.
- Valve Frames: L605 panels (0,3–0,8 mm thick) shape cardiac implants (20–35 mm Ø).
- Thickness: 0,2–5 mm
- Size: Up to 400 × 400 mm
- Weight: 41,5 g/100 cm² (at 0,5 mm, L605), 42 g/100 cm² (MP35N)
- Çekme Dayanımı: 900–1300 MPa (L605), 1000–1400 MPa (MP35N)
- Hardness: 350–500 HV (L605), 400–550 HV (MP35N)